V Shape SS 310 Refractory Anchor With Mn≤2.00% Density 7.96g/Cm3
V Anchor Refractory is a type of refractory product with superior thermal shock, anti-corrosion and high temperature resistance. It is made of high-quality stainless steel 310 and has a density of 7.96g/cm3. The product contains ≤0.08% C and 19-22% Ni, and its melting temperature is 1410-1415℃. V Anchor Refractory is the perfect choice for applications that require superior thermal shock, anti-corrosion and high temperature resistance. It is ideal for use in industrial, commercial and residential applications. It is an ideal refractory product for any application where superior thermal shock, anti-corrosion and high temperature resistance are of the utmost importance.
| Property | Value |
|---|---|
| Name | V Shape SS 310 Anchor Refractory |
| Si | ≤1.5% |
| Cr | 24-26% |
| S | ≤0.03% |
| Mn | ≤2.00% |
| P | ≤0.04% |
| C | ≤0.08% |
| Melting Temperature | 1410-1415℃ |
| Ni | 19-22% |
| Density | 7.96g/cm3 |
FALTHFUL's V Shape SS 310 Refractory Anchors are a highly durable, anti-corrosion, fire resistant refractory material, manufactured from SS310, which has a density of 7.96g/cm3, and contains a low amount of Si, C, and Ni (Si ≤1.5%, C ≤0.08%, Ni 19-22%). It is available in 500KGS minimum order quantity, and is packaged in wooden cases for delivery within 25 days. Payment terms are L/C or T/T. FALTHFUL's V Anchor Refractory product is a reliable and long-lasting solution for a variety of applications, with a supply ability of 20TON/25DAYS.
V Shape SS 310 Refractory Anchor products are packaged and shipped in accordance with the following guidelines:
1.All products must be packaged securely in a cardboard box .
2.The box must be clearly labeled with the product name.
3.The box must be securely sealed.
4.The box must be placed in a larger box for shipping.
5.The larger box must be clearly labeled with the product name and quantity.
6.The box must be shipped using a reliable courier service.
Our products are sold all over the world, you can rest assured.